» » Precision gauge strips steel 1.1274 sheet
Precision gauge strips steel 1.1274 sheet
See larger image
I have seen this product cheaper elsewhere.

Precision gauge strips steel 1.1274 sheet

-CLINQ XC100 FEUIL

With a carbon content of over 1%, this material is very well suited for feeler gauge strips and precision foils as well as highly stressed springs that are not subject to any corrosion requirements.

Quantity : 
+
-
Available Dispatched within 10 days

FORMAT-EPAISSEUR EN MM-1278

36.90€ Excluding VAT
44.28€ VAT INCLUDED
Add to quotation requests

  FORMAT
EPAISSEUR EN MMPar 10 feuilles Format 25X300Par 10 feuilles Format 50X300
0.01044.28€61.61€
0.02026.38€35.27€
0.03018.46€27.17€
0.04018.46€24.96€
0.05014.68€22.24€
0.06014.12€18.60€
0.07014.29€19.10€
0.08014.46€19.10€
0.09014.50€19.10€
0.10012.96€17.29€
0.120 18.11€
0.15012.96€18.11€
0.180 18.25€
0.20012.96€17.70€
0.25013.45€18.25€
0.30013.45€18.25€
0.350 19.90€
0.40014.68€19.90€
0.450 21.18€
0.50015.76€19.90€
0.60017.28€35.28€
0.70018.31€35.82€
0.80018.90€35.82€
0.90018.90€37.20€
1.00019.44€31.97€
Facebook - Partager
LinkedIn
Viadeo
description
Notice

Material Datasheet                                                                                Issue: October 2015

Download datasheet here:

https://sbc-trading.fr/images/Image/File/Precision-gauge-strip-AISI-1095.pdf

Hardened Spring Steel W.-Nr. 1.1274

 

  1. Applications:

With a carbon content of over 1%, this material is very well suited for feeler gauge strips and precision foils as well as highly stressed springs that are not subject to any corrosion requirements. In particularly high-quality designs,

as the only carbon steel, 1.1274 is suitable for shock absorbers and flapper valves.

 

Further applications: wear bars, doctor blades

 

The alloy 1.1274 is suitable for springs according to DIN 17 222 (new: DIN EN 10 132-4).

 

In thicknesses of more than 1.0 mm we can supply the hardened tool steel W.-Nr. 1.2003.

 

2.  Material codes:

German Norm:             1.1274 C100S+QT (former known as Ck101) AISI:                      1095

ASTM:                           G 10950

Engl. Norm:                  95 (B.S. 5770 Part 1)

Franz. Norm:                XC100

Japan. Norm:               SK 4-CSP (Norm G 4802)

 

3.  Chemical composition: *

C:

max. 1.05 %

Si:

0.15-0.30 %

Mn:

0.30-0.45 %

P:

max. 0.02 %

S:

max. 0.02 %

Cr:

ca. 0.10 %

* the exact composition of each batch can be documented by a material certificate

2.2 or 3.1 according to DIN EN 10 204.

 

4.  Delivery condition:

Condition:                     hardened and tempered (martensitic structure) Surface:white polished, please ask for Ra-values

Flatness:                       mostly P2 (max. 0,30% of the strip width)

Tensile strength:         see table (from 1400-1600 to 2000-2200 N/mm² depending on thethickness)

 

Further mechanical data: see chapter 7 and 8.

 

5.  Sizes:

Thicknesses:                0.02-2.00 mm (between 1.10 and 2.00mm only width 12.7mm)

 

Raw material width:    from 12.7 up to 305 mm (see table)

Standard widths:         6 – 12.7 – 25 – 50 and 305 mm (not in all thicknesses)

 

Edges:                           in widths 6 and 12.7 mm round edges in thicchnesses from

0.25 to 2.0mm, all other sizes with cut edges

 

The following sizes are available from stock (without obligation), status: October 2015:

 

Thicknes s

in mm

Maximum width

in mm

Tensile strength in N/mm²

Annotation

0,02

12,7

2000-2200

 

0,03

ca. 102

2000-2200

 

0,04

ca. 102

2000-2200

 

0,05

ca. 145

2000-2200

 

0,06

ca. 120

2000-2200

 

0,07

ca. 120

2000-2200

 

0,08

ca. 120

2000-2200

 

0,09

ca. 120

2000-2200

 

0,10

305

2000-2200

 

0,12

ca. 240

2000-2200

 

0,15

305

2000-2200

 

0,18

ca. 248

2000-2200

 

0,20

305

1800-2100

 

0,25

305

1800-2100

 

0,30

305

1800-2100

 

0,35

305

1800-2000

 

0,40

305

1600-1900

 

0,45

50

1600-1900

 

0,50

305

1600-1900

 

0,55

12,7

1600-1900

 

0,60

305

1600-1800

 

0,65

12,7

1600-1800

 

0,70

305

1600-1800

 

0,75

12,7

1600-1800

ca. 300 mm Coil in Ck75 16-1800 N/mm²

0,80

305

1600-1800

 

0,85

12,7

1600-1800

ca. 200x1000 mm in Ck75/85

0,90

305

1600-1800

 

0,95

12,7

1600-1800

ca. 200x1000 mm in Ck75/85

1,00

305

1600-1800

 

1,10-2,00

12,7

1400-1600

in Schritten von 0,10 mm steigend

 

In the thicknesses from 1.0 to 5.03 mm we have the hardened tool steel 1.2003 (75Cr1) on stock.

 

6.  Tolerances:

Thickness tolerance: T3 Widthtolerance:       B2

Straightness:                normal

Flatness:                       P3 = 0,2% of the strip width

 

7.  Further mechanical data:

Yield str. Rp0,2 :         approx. 90 % of the tensile strength ElongationA 80:       no data available

 

Fatigue strength:         high fatigue strength, suitable for shock absorber valves and flappervalves

 

If good tumbling is done, the following values can be achieved: Reversed bending stress (Mean stress = 0):

620-680 MPa at a failure rate of 5 %.

 

Fluctuating bending stress (Minimum stress = 0):

520-580 MPa at a failure rate of 5 %

 

As the fatigue strength depends on different factors like the corrosive conditions and the edge treatment, no definitive endurance limit values can be guaranteed.

 

Please ask if the requested batch meets the high demands for shock absorber valves or compressor valves.

 

The operation temperature should not exceed 200°C.

Please remember that the modus of elasticity decreases at higher temperatures.

For higher operation temperatures we suggest the stainless hardened steels like the alloys 1.4031Mo (up to 0.80 mm thickness) and 1.4034 (from 1.0 to approx. 10.0 mm thickness)

 

8.  Physical properties (for the alloy 1.1248 = C75S)

Density:                                 7,9 g/cm³

Thermal conductivity:          49 W/(m °C) at 20 °C

Spec. heat capacity:           460 J/(kg °C) mean value at 50 – 100 °C Thermalexpansion:       10,5 x 10 -6 (between 30 - 100 °C)

11,5 x 10 -6 (between 30 - 200 °C)

12,5 x 10 -6 (between 30 - 300 °C)

Electric resistance:              approx. 0,20 Ohm x mm²/m (for 1.1231= C67S hardened)

 

Modus of elasticity:             210 000 MPa at 20 °C

Relative permeability µr:    maximum 400 (for 1.1231= C67S hardened)

 

9.  Blanking

We recommend a punch-to-die clearance of 4-10 % of the strip thickness.

The corner radius should be at least 0.25 mm and the punching die should be at least twice the strip thickness.

After blanking a stress relieving at a maximum temperature of 250°C for 30-60 minutes is suggested.

The pieces should then be tumbled to receive a good edge roundness. We suggest to produce the pieces by photo etching.

10.  Laser cutting

As the material melts at the edge during laser cutting, a higher hardness and therefore a lower toughness at the cutting zone is possible.

We suggest to produce critical pieces by water jet cutting.

 

11.  Photo etching

The alloy 1.1274 can be etched easily.

 

12.  Bending

As this material is supplied in the hardened and tempered condition, the rolling direction is not important regarding the bending.

 

Bending radius:           minimum 10 times of the strip thickness.

Spring back angle:      As the spring back angle depends on several factors, bending tests are necessary. As guidance an angle of 10° at a strip thickness of 0.20 mm and an angle of 20° at a strip thickness of 0.60 mm can be expected.

 

13.  Flat grinding

The alloy 1.1274 is magnetisable and can be fixed by magnetic clamping devices of flat grindingmachines.

 

14.  Welding

Due to the high content of carbon the alloy 1.1274 should not be welded.

 

15.  Corrosion resistance

The alloy 1.1274 is not corrosion resistant. We supply this alloy with a light oil film. If used at normal conditions this alloy needs to be painted or galvanized.

 

Important Annotation

The specifications which are given in this technical information sheet about the condition and application of the alloys are only for reference and are no confirmation about certain performances and characteristics.

The information correspond to our own experiences and experiences of our suppliers.

We can not guarantee for the results during processing and utilisation.

 