» » Precision gauge strips AISI 310 COILWARE
Precision gauge strips AISI 310 COILWARE
See larger image
I have seen this product cheaper elsewhere.

Precision gauge strips AISI 310 COILWARE

-CLINQ INOX ROUL

Cold-rolled, stainless spring steel strip, mat. no. 1.4310

Quantity : 
+
-
Available Dispatched within 10 days

FORMAT-EPAISSEUR EN MM-1276

52.39€ Excluding VAT
62.87€ VAT INCLUDED
Add to quotation requests

  FORMAT
EPAISSEUR EN MM12.7mm x 5M50mm x 5M100mm x 5M150mm x 5M305 x 1M600mm x 1M
0.005mm62.87€128.34€    
0.010mm53.10€89.63€149.51€   
0.015mm  137.04€   
0.020mm34.31€52.37€77.40€   
0.025mm   115.33€  
0.030mm14.86€ 71.20€ 0.00€ 
0.035mm  77.51€   
0.040mm14.86€ 78.36€ 0.00€ 
0.045mm  164.70€   
0.050mm15.31€37.99€53.78€81.00€0.00€0.00€
0.055mm  107.10€   
0.060mm10.68€ 61.30€ 0.00€ 
0.070mm10.68€ 61.30€ 0.00€ 
0.075mm   78.00€  
0.080mm10.68€ 61.30€ 0.00€ 
0.090mm10.68€ 61.30€ 0.00€ 
0.100mm11.36€28.24€54.13€80.66€18.42€0.00€
0.110mm11.70€ 55.97€   
0.120mm  61.04€   
0.130mm  61.04€   
0.150mm12.88€28.24€54.67€81.13€23.53€66.71€
0.160mm  65.52€   
0.170mm  65.52€   
0.190mm  65.52€   
0.200mm12.67€34.57€69.76€98.27€22.25€82.08€
0.220mm  71.20€   
0.230mm  74.16€   
0240mm  78.08€   
0.250mm12.67€36.52€68.29€98.27€36.00€127.80€
0.260mm  84.60€   
0.300mm17.27€34.27€69.38€98.27€36.00€116.64€
0.350mm  78.13€   
0.400mm22.42€46.80€75.60€112.18€43.73€128.95€
0.450mm17.74€40.42€91.00€   
0.500mm17.74€46.25€85.50€126.97€47.64€99.08€
0.550mm  108.18€   
0.600mm27.98€61.82€106.26€151.66€77.28€143.88€
0.650mm  133.31€   
0.700mm28.90€64.57€118.85€170.64€ 152.56€
0.750mm  147.60€   
0.800mm31.06€68.53€127.68€190.27€83.76€159.88€
0.850mm  149.22€   
0.900mm  129.10€232.48€85.14€ 
0.950mm  151.15€   
1.000mm31.15€71.98€135.90€232.80€101.04€179.27€
      
Facebook - Partager
LinkedIn
Viadeo
description
Notice

Material Datasheet                                                                                               Issue: October 2015

 

Download datasheet here

 

https://sbc-trading.fr/images/Image/File/Precision-gauge-strips-AISI-301.pdf

 

Temper rolled Spring Steel W.-Nr. 1.4310

 

1. Applications:

The alloy 1.4310 (AISI 301) has a good corrosion resistance due to a content of 17% Chromium and 7% Nickel. A high tensile strength is obtained by cold rolling. Compared to alloy 1.4301 (AISI 304) a much higher tensile strength of more than 2000 N/mm² can be reached. Because of this, the alloy 1.4310 is suitable for stainless feeler gage stock, precision foils, stainless springs and parts of higher strength. This alloy is little magnetic and can not be hold by magnetic tables of grinding machines. Available in more than 60 thicknesses between 0.003 and 3.0 mm and in different tensile strengths.

 

Further applications:

welded steel belts, transport belts

 

The alloy 1.4310 is suitable for spring according to DIN 17 224 (new: DIN EN 10 151).

 

At high demands for hardness and wear resistance we suggest the alloys 1.4031Mo (up to

0.80 mm thickness) and 1.4034 (1.0 to approx. 8.0 mm thickness).

 

2. Material codes:

 

German Norm:

1.4310, X10CrNi 17-7

AISI:

301

ASTM:

S 30100

Engl. Norm:

301S21

French Norm:

Z 12 CN18-09

Japan. Norm:

SUS 301

 

3. Chemical composition (nominal): *

C:

0.05-0.15 %

Si:

max. 2.00 %

Mn:

max. 2.00 %

P:

max. 0.045 %

S:

max. 0.015 %

Cr:

16-19 %

Ni:

6-9.5 %

Mo:

max. 0.80 %

 

* the exact composition of each batch can be documented by a test certificate 2.2 or 3.1 according to DIN 10 204

 

4.  Delivery condition:

Condition:                     temper rolled (austenitic and partially martensitic), not hardenable Surface:   2H, Ra maximal 0,3 µm (depending of the roughness of the working

roll)

Tensile strength:         1100 up to more than 2000 N/mm²

 

The tensile strength can be increased by annealing at 330-370°C (approx. 4 hours) for 100- 300 N/mm² (depending on the primary tensile strength of the material).

 

Further mechanical data: see chapter 7 and 8.

 

5.  Sizes:

Thickness:                    0,003-3,00 mm

Raw material width:    depending on thickness 50 up to approx. 1000 mm in several tensile strengths

Standard widths:         10,0 – 12,7 – 25 – 50 – 100 – 150 mm in tensile strength 15-1700 Edges:      cut

Lengths:                        variable lengths from 5 to 10 000 mm or as Coil

 

The following maximum widths are available from stock: (without obligation, Issue: November 2014)

 

Thick- ness

UTS 1100-

1300

UTS 1300-

1500

UTS 1500-

1700

UTS 1900-

2100

Annotations

0,003

 

 

 

 

ca. 50 mm temper rolled

0,005

 

 

 

 

ca. 100 mm temper rolled

0,008

 

 

 

 

ca. 100 mm temper rolled

0,01

 

 

205

 

 

0,015

 

 

100

 

 

0,02

 

 

100

 

 

0,025

 

 

300

 

 

0,03

 

ca. 300

100

 

 

0,035

 

 

100

 

 

0,04

 

ca. 300

100

 

 

0,045

 

 

100

 

 

0,05

 

ca. 300

305

 

 

0,055

 

 

100

 

 

0,06

 

 

305

 

 

0,07

 

 

305

 

 

0,075

 

 

305

 

 

0,08

 

 

305

 

 

0,09

 

 

305

 

 

0,10

ca. 300

ca.300+1000

305+610

ca. 300

 

0,11

 

 

305

 

 

0,12

 

 

305

 

 

0,13

 

 

305

 

 

0,14

 

 

305

 

 

0,15

ca .300

300+1000

305+610

 

 

0,16

 

 

305

 

 

0,17

 

 

305

 

 

0,18

 

 

305

 

 

0,19

 

 

305

 

 

0,20

ca. 300+600

300+1000

305+610

ca. 300

 

0,21

 

 

305

 

 

0,22

 

 

305

 

 

0,23

 

 

ca. 205

 

 

0,24

 

 

305

 

 

0,25

ca .300

300+1000

305+610

 

 

0,26

 

 

305

 

 

0,27

 

 

305

 

 

0,28

 

 

305

 

 

 

Thick- ness

UTS 1100-

1300

UTS 1300-

1500

UTS 1500-

1700

UTS 1900-

2100

Annotations

0,29

 

 

305

 

 

0,30

ca.300+600

300+1000

305+610

ca. 300

+ 620x1000 F13-1500

0,325

 

 

only 12,7

 

 

0,35

 

 

305

 

 

0,40

ca. 300

300+1000

305+610

 

+ 620x1000 F13-1500

0,45

 

 

305

 

 

0,47

 

 

ca. 300

 

 

0,50

ca. 300

300+1000

305+610

 

+ 630x1000 F13-1500

0,55

 

 

305

 

 

0,60

ca .300

 

305+610

 

 

0,65

 

 

305

 

 

0,70

 

 

305+610

 

 

0,75

 

 

250x1000

 

 

0,80

ca. 300

 

305

 

+ 600x1000 F11-1300/15-1700

0,85

 

 

305

 

 

0,90

 

 

305

 

 

0,95

 

 

305

 

 

1,00

ca. 300

 

305

 

+ 600x1000 F11-1300/15-1700

1,10

 

 

100x500

 

 

1,20

300x2000

 

100/150x500

 

 

1,30

 

100x500

 

 

 

1,40

 

100x500

 

 

 

1,50

300x2000

100/150x500

 

 

 

1,60

 

100x500

 

 

 

1,70

 

100x500

 

 

 

1,80

 

100/150x500

 

 

+ 250x1000 F 13-1500

1,90

 

100x500

 

 

 

2,00

300x2000

100/150x500

 

 

 

2,50

300x2000

 

 

 

 

3,00

300x2000

 

 

 

 

 

 

6.  Tolerances:

Thickness tolerance: DIN EN 9445 Table 1 or T3 (for U.T.S. 15-1700 N/mm²) Widthtolerance:        according to DIN EN 9445

Straightness:                normal

Flatness:                       wave height max. 1,0 mm

 

7.  Further mechanical properties

Yield Str. Rp0,2 :         depending on tensile strength Elongation A 80:     depending on tensile strength

 

If good tumbling is done, the following values can be achieved: Reversed bending stress (Mean stress = 0):

550 MPa (50 % of the tested samples survive 2 million cycles at normal environment), if bending direction is at a 90° angle to the rolling direction

 

Fluctuating bending stress (Minimum stress = 0):

420 MPa (50 % of the tested samples survive 2 million cycles at normal environment), if bending direction is at a 90° angle to the rolling direction

 

As the fatigue strength depends on different factors like the corrosive conditions and the edge treatment, no definitive endurance limit values can be guaranteed.

At high forces or bending not in the right angle to the rolling direction hardened steels like the alloy 1.4031Mo are strictly recommended.

 

The operation temperature should not exceed 120-250°C (compare to DIN 17224 – stainless strip steel for springs). Please remember that the modus of elasticity decreases at higher temperatures.

 

8.  Physical properties:

Density:                                 7,9 g/cm³

Thermal conductivity:          15-19 W/(m °C) depending on the temperature Spec.heat capacity:       500 J/(kg °C) mean value at 50 – 100 °C Thermal expansion:   15,5 x 10 -6 (between30 - 100 °C)

16,0 x 10 -6 (between 30 - 200 °C)

16,5 x 10 -6 (between 30 - 300 °C) Electricresistance:       0,73 Ohm x mm²/m

 

Modus of elasticity:             185 000 MPa at 20 °C

 

Relative Permeability µr:    maximal 24 (further data: see chapter 13)

 

9.  Blanking

We recommend a punch-to-die clearance of 4-10 % of the strip thickness.

The corner radius should be at least 0.25 mm and the punching die should be at least twice the strip thickness.

The pieces should then be tumbled to receive a good edge roundness.

 

10.  Laser cutting

This alloy can be laser cut without problems.

 

11.  Photo etching

The alloy 1.4310 can be etched easily.

 

12.  Bending

As the high hardness of 1.4310 is obtained by temper rolling, the rolling direction has a big influence on the bending.

The suggested minimum bending radius also depends on the tensile strength. Bending at right angle (90°) to the rolling direction:

 

11-1300

13-1500

15-1700

>1700 N/mm²

Up to 0,25 mm

1,0 x t

1,50 x t

2,0 x t

2,5 x t

0,25-0,50 mm

1,0 x t

2,0 x t

2,5 x t

3,0 x t

0,50-0,75 mm

2,0 x t

2,5 x t

3,0 x t

3,5 x t

0,75-1,00 mm

2,5 x t

3,0 x t

4,0 x t

Not recommended

t = Strip thickness

 

Bending parallel to the rolling direction:

 

11-1300

13-1500

15-1700

>1700 N/mm²

Up to 0,25 mm

2,5 x t

3,0 x t

6,5 x t

9,0 x t

0,25-0,50 mm

3,0 x t

4,0 x t

9,0 x t

9,5 x t

0,50-0,75 mm

4,0 x t

5,0 x t

9,5 x t

11,0 x t

0,75-1,00 mm

5,0 x t

7,0 x t

10,0 x t

Not recommended

t = strip thickness

 

We suggest the tensile strength of 11-1300 N/mm² for bended pieces

 

13.  Flat grinding

In the temper rolled condition this alloy is only little magnetic and can not be holy by magnetic clamping devices of flat grinding machines.

 

The alloy 1.4310 has an austenitic structure in the annealed condition and is therefore nearly unmagnetic. The temper rolling leads to a change in the structure from austenitic to martensitic which causes an increase of magnetizability.

 

As this depends on several factors like the deformation degree, the material temperature during rolling and the chemical composition of the alloy, no specific data can be given.

 

At a deformation degree of 50%, the relative permeability should be not more than 10 to 18, and at a deformation degree of 70% the relative permeability should be not more than 15 to 24 (at 200H).

 

14.  Welding

The alloy 1.4310 can be welded easily. At the weldseam a change in the structure occurs due to the welding heat which decreases the strength.

Due to a content of approx. 0.10% of Carbon local corrosion at the weldseam is possible.

For critical applications the alloy 1.4404 (AISI 316L) with a verly low content of Carbon of less than 0.03% is recommended.

 

15.  Corrosion resistance

This alloy is in the group 4 in the Nirosta-table of corrosion resistance of stainless steels (see www.nirosta.de/Publikationen). This alloy is less resistant than the alloys 1.4404 (in group 5), but better resistant than the grades 1.4031Mo and 1.4034 (both in group 1).

 

Nirosta is a registered trade mark of ThyssenKrupp AG.

 

Please check there and by tests if the alloy 1.4310 is resistant enough for your application. As alternative, the alloy 1.4404 (AISI 316L) is available in the strength 11-1300 N/mm² in the thicknesses 0,01-0,02-0,05-0,10-0,15-0,20-0,25-0,30-0,40 and 0,50 mm.

 

Important Annotation

The specifications which are given in this technical information sheet about the condition and application of the alloys are only for reference and are no confirmation about certain performances and characteristics.

The information correspond to our own experiences and experiences of our suppliers. We can not guarantee for the results during processing and utilisation.

 

Back to top
description
Notice

Reviews about this Precision gauge strips AISI 310 COILWARE (0 reviews)

There is no review for this item, add the first one.
[Add your review]
Back to top

Customers who bought Precision gauge strips AISI 310 COILWARE also bought :