» High speed steel round HS.6-5-2-5
High speed steel round HS.6-5-2-5
See larger image
I have seen this product cheaper elsewhere.

High speed steel round HS.6-5-2-5

-BAR5

USA: (AISI M35)
Europe: HS.6-5-2-5
Werkstoff W.Nr. 1.3243
AFNOR Z90WDKCV6.5.5.4.2

Quantity : 
+
-
Available Dispatched within 10 days

dimension-prix-1912

6.06€ Excluding VAT
7.27€ VAT INCLUDED
Add to quotation requests

  dimension
prixprix
ø 1,5 x 507.27€
ø 2 x 507.27€
ø 2 x 1007.66€
ø 2,5 x 607.66€
ø 3 x 606.62€
ø 3 x 1007.79€
ø 3 x 1207.92€
ø 3,5 x 606.11€
ø 3,5 x 1208.32€
ø 4 x 806.36€
ø 4 x 1608.45€
ø 4,3 x 808.17€
ø 4,5 x 806.62€
ø 5 x 806.62€
ø 5 x 1609.86€
ø 5,5 x 807.54€
ø 6 x 506.88€
ø 6 x 807.40€
ø 6 x 16010.78€
ø 6,5 x 1009.74€
ø 8 x 808.32€
ø 8 x 16014.54€
ø 10 x 8012.60€
ø 10 x 16017.80€
ø 11 x 8015.71€
ø 11 x 16025.44€
ø 12 x 8014.81€
ø 12 x 16022.07€
ø 13 x 16026.74€
ø 14 x 10019.34€
ø 14 x 16026.88€
Facebook - Partager
LinkedIn
Viadeo
description
Notice

High Speed Steel HS.6-5-2-5

 

C

Cr

Mo

W

Co

V

0,93

4,2

5,0

6,4

4,8

1,8

 

 

 


DESCRIPTION
E M35 is a high speed cobalt steel offering good hot hardness. Its composition allows a good compromise between hardness and resilience. E M35 has good grinding ability

 

 

HEAT TREATMENT

Soft annealing in a protected atmosphere at 850-900 ° C for 3 hours, followed by slow cooling in steps of 10 ° C per hour up to 700 ° C, then air cooling.

Stress relieving annealing from 600 ° C to 700 ° C Holding time approx. 2 hours, slow cooling to 500 ° C.

Quenching in a protected atmosphere with preheating in two stages at 450-500 ° C and 850-900 ° C and austenitization at a temperature chosen according to the hardness.

Two tempers at 560 ° C are recommended (maintain at least one hour each time).

 

Back to top
description
Notice

Reviews about this High speed steel round HS.6-5-2-5 (0 reviews)

There is no review for this item, add the first one.
[Add your review]
Back to top
Products